Brahma Lab PLA Matte Dual Color 3D Printer Filament

Description Brahma Lab PLA Matte Dual Color 3D Printer Filament is a premium 1.75mm PLA filament designed to deliver stunning, professional-quality prints with ease. Featuring a unique matte texture and a dual-color shifting effect, your models gain an eye-catching appearance that changes shades when viewed from different angles. This specialty filament is perfect for 3D printed ornaments, toys, crafts, decorative models, and artistic designs where aesthetics matter most. Engineered for smooth extrusion, excellent layer adhesion, and dimensional accuracy, this filament ensures consistent results across a wide range of FDM 3D printers. With low shrinkage, strong mechanical properties, and reliable thermal stability, it is suitable for hobbyists, makers, and professionals who want to achieve high-quality dual-color matte prints without complications. Whether you are creating custom 3D printed gifts, display models, or functional prototypes, Brahma Lab PLA Matte Dual Color filament brings your ideas to life with style and precision. Matte Dual-Color Finish – Achieve premium-looking models with a unique two-tone shifting effect that changes shades depending on the viewing angle, combined with a smooth matte surface for elegant aesthetics. 75mm Filament Diameter – Precisely manufactured with ±0.02mm tolerance, ensuring stable extrusion, smooth feeding, and compatibility with most FDM 3D printers. High Mechanical Strength – With a tensile strength of 43 MPa and excellent durability, this filament produces strong, reliable prints suitable for both decorative and functional parts. Low Shrinkage & Dimensional Accuracy – With a shrinkage rate of only 0.1–0.3%, this filament minimizes warping and maintains precise geometry for consistent print quality. Thermal Stability – Offers heat deflection up to 53°C and a glass transition temperature of 58.8°C, ensuring stable performance during long print runs. Smooth Extrusion & Layer Bonding – Optimized melt flow rate (10 g/10min) provides excellent layer adhesion, reducing stringing and enhancing overall print surface finish. Wide Compatibility – Works seamlessly with most FDM/FFF 3D printers, making it suitable for hobbyists, makers, designers, and professionals. Property Test Method Test Condition S.I. Units Typical Values Tensile Strength (X-Y) ISO527/2 50mm/min MPa 43 Young’s Modulus (X-Y) ISO527/2 1mm/min MPa / Elongation at Break (X-Y) ISO527/2 50mm/min % 11 Flexural Strength (X-Y) ISO178 2mm/min MPa 69 Flexural Modulus (X-Y) ISO178 2mm/min MPa 3572 IZOD Impact Notched (X-Y) ISO180 23°C KJ/m2 4.7 IZOD Impact Notched (Z-X) ISO180 23°C KJ/m2 / Shore Hardness ISO868 23°C HD 85 Heat Deflection (HDT) ISO75 0.45MPa °C 53 Glass Transition (Tg) ISO11357-3 10°C/min °C 58.8 Melting Point ISO11357-3 10°C/min °C 162.6 @5% Decomposition Temp. ISO11358 20°C/min °C ≥374 Vicat Softening Temp. ISO306 5kg, 50°C/h °C 54 Mold Shrinkage ISO294 23°C % 0.1-0.3 Coefficient of Thermal Expansion ISO11359-2 / µm/(m·°C) 101×10-6 Melt Flow Rate ISO1133 190°C/2.16kg g/10min 10 Density ISO1183 23°C g/cm3 1.3 Volume Resistivity IEC60093 – ohm-cm 2.90E 15 Dielectric Constant IEC60250 1kHz / 1.51 Flammability UL94 1.5mm Class HB Parameter Range Nozzle Print Temp. (°C) Temperature °C Speed mm/s 205-215 50-150 215-245 100-230 Print Platform Temp. 50-60°C Print Platform Material Normal Print Platform Treatment No processing required Cooling Fan On Raft Distance 0.4-0.6mm Retraction Distance 0.8-1.2mm Retraction Speed 30-40mm/s Room Temp. Normal temperature Support Material PVA Drying Temp. 50°C To explore varieties of Brahma Lab filaments – Click hear